Basic Info.
Thermal Rating
H 180
Thickness
0.0125mm, 0.025mm
Young’s Modulus
>=3.1gpa
Coefficient of Thermal Expansion
<27ppm/Degree
Width
520mm, 1040mm, 1028mm
Type
Insulation Film
Chemistry
Organic Insulation
Classification
Organic Insulating Material
Certification
ISO9001
Transport Package
Carton and Pallet
Specification
1-7mil
Origin
China
HS Code
3920920000
Production Capacity
15000kg/Month
Product Description
Shandong Xinhongyun New Material Technology Co., Ltd.Located in Weifang city, Shandong province., is an ISO-certified professional & reliable manufacture of electrical insulation materials-BOPI FILM(polyimide film). our annual production capacity is 150-200MT.main thickness 12.5um,25um & 50um, main width 514mm,520mm,1028mm&1040mm.main color: yellow, red, matte black.
we have a strict quality inspection system, we trust we can supply you the best quality product with high quality
Polyimide (PI) is a polymer of imide monomers, also known as heat resistant film or high-temperature film. With their high heat resistance, polyimide enjoys diverse applications in roles demanding rugged organic materials. Polyimide film is ideal for insulating circuit boards, high-temperature powder coating, and transformers manufacturing.
Polyimide film provides excellent electrical, thermal, physical, and chemical properties over a wide temperature range between -269ºC (-452ºF) and 400ºC (752ºF) making them superior for electrical insulation applications. Polyimide film can be laminated, metalized, punched, formed, or adhesive coated. It is the recommended choice for applications that require an all-polyimide film with an excellent balance of properties over a wide range of temperatures.we can provide both standard and custom polyimide film solutions for a customer depending on their needs.
| NO. | Items | Uint | Request | Analysis result |
| 1 | Appearance | -- | Film surface smooth, no obvious defects and debris, clean edge without damage | Pass |
| 2 | Thickness | μm | 12.5±0.5 | 12.9 |
| 3 | Tensile strength | Mpa | MD≥220 | 225 |
| TD≥220 | 223 | |||
| 4 | Elongation at break | % | MD≥50 | 55 |
| TD≥50 | 63 | |||
| 5 | Young's Modulus | MPa | MD≥3100 | 3465 |
| TD≥3100 | 3285 | |||
| 6 | Electric strength | MV/m | ≥235 | 343 |
| 7 | Shrinkage | % | MD±0.2 | 0.17 |
| TD±0.2 | -0.01 | |||
| 8 | Surface tension | Dyne/cm | ≥58 | 60 |
| NO. | Items | Uint | Request | Analysis result |
| 1 | Appearance | -- | Film surface smooth, no obvious defects and debris, clean edge without damage | Pass |
| 2 | Thickness | μm | 25±1 | 24.9 |
| 3 | Tensile strength | Mpa | MD≥165 | 219 |
| TD≥165 | 201 | |||
| 4 | Elongation at break | % | MD≥50 | 62 |
| TD≥50 | 60 | |||
| 5 | Young's Modulus | MPa | MD≥3000 | 3244 |
| TD≥3000 | 3225 | |||
| 6 | Electric strength | MV/m | ≥235 | 284 |
| 7 | Shrinkage | % | MD±0.1 | -0.02 |
| TD±0.1 | -0.03 | |||
| 8 | Surface tension | Dyne/cm | ≥58 | 60 |
Product & packing picture
Lead Time:
| Quantity(KGS) | 1-20 | 21-500 | 501-2000 | >2000 |
| Est.Time(Days) | 5 | 10 | 15 | To be negotiated |
Applications
Wire&cable Insulation, slot liner insulation,interlayer insulation in Motor,transformer etc.
Backing material for Polyimide coating or composites
Flexible Printed Circuits Board(F-PCB)
Polyimide Label
Polyimide tubing
FCCL membrane PI in LED lights PCB
Coverlay film in FPC/PCB
High-temp cables wrapped PI PI in die-cutting
PI in battery Black PI tape
CERTIFICATIONS
FAQ
Q1:Are you a trading company or manufacturer?
We are a manufacturer, We have our own workshop producing electrical insulation polyimide film.
Q2: Can you send samples for testing?
A4 size Samples & Small rolls are free supplied, customers just need to pay a litter shipping charge.
Q3: How can you guarantee the quality of mass goods is the same as the sample sent to me before?
We kept another same sample and marked it on the company when we sent it to the customer. So our products will be based on and also we will test the product before shipment.
Q4: Which package do you use?
The package is an important part to avoid goods breaking in transportation. We will choose suitable packing depending on the materials.
Package&Storage:
Packed in rolls and carton; store at room temperature; avoid fire. The storage period is 12 months.
If you are interested please do not hesitate to contact us.